Makrolon®
PC
2805
Product information | |
---|---|
Manufacturer | Covestro AG |
Other Certificates | |
Part Marking Code | |
Color | |
Material Shape | |
Process | |
Viscosity | |
FR | |
specification | |
Features | |
Application | |
Additives | |
UL File NO. | |
Certificate |
Physical property | Standard | Value | Unit |
---|---|---|---|
Density | ISO 1183 | kg/m³ | |
Shrinkage Flow 60x60x2mm 50MPa | ISO 294 | % | |
Shrinkage xFlow 60x60x2mm 50MPa | ISO 294 | % | |
Shrinkage Flow | ISO 2577 | % | |
Shrinkage xFlow | ISO 2577 | % | |
Water Absorption 23°C | ISO 62 | % | |
Water Absorption 23°C 50RH Equilibrium | ISO 62 | % | |
Melt Index 300°C 1.2kg | ISO 1133 | cm³/10min | |
Melt Index 300°C 1.2kg | ISO 1133 | g/10min | |
Bulk Density | ISO 60 | kg/m³ | |
Water Vapor Transmission 23°C 85RH 100μm Film | ISO 15106 | g/m²/24hr | |
Oxygen Transmission 100μm Film | ISO 2556 | cm³/(m²-24hr-bar) | |
Oxygen Transmission 25.4μm Film | ISO 2556 | cm³/(m²-24hr-bar) | |
Nitrogen Transmission 100μm Film | ISO 2556 | cm³/(m²-24hr-bar) | |
Nitrogen Transmission 25.4μm Film | ISO 2556 | cm³/(m²-24hr-bar) | |
Carbon Dioxide Transmission 100μm Film | ISO 2556 | cm³/(m²-24hr-bar) | |
Carbon Dioxide Transmission 25.4μm Film | ISO 2556 | cm³/(m²-24hr-bar) |
Hardness | Standard | Value | Unit |
---|---|---|---|
Ball Indentation Hardness | ISO 2039 | N/mm² |
Mechanical behavior | Standard | Value | Unit |
---|---|---|---|
Tensile Modulus 1.0mm/min | ISO 527 | MPa | |
Tensile Strength Yield 50mm/min | ISO 527 | MPa | |
Tensile Strength Break 50mm/min | ISO 527 | MPa | |
Elongation Yield 50mm/min | ISO 527 | % | |
Elongation Break 50mm/min | ISO 527 | % | |
Elongation Break 50mm/min | ISO 527 | % | |
Tensile Creep Modulus 1hr | ISO 899 | MPa | |
Tensile Creep Modulus 1000hr | ISO 899 | MPa | |
Flexural Strength 2.0mm/min | ISO 178 | MPa | |
Flexural Strength 3.5%Strain 2.0mm/min | ISO 178 | MPa | |
Flexural Modulus 2.0mm/min | ISO 178 | MPa | |
Flexural Strain 2.0mm/min | ISO 178 | % | |
Izod Notch Impact 23°C 3.0mm Partial break | ISO 180 | kJ/m² | |
Izod Notch Impact -30°C 3.0mm Complete Break | ISO 180 | kJ/m² | |
Charpy Notch Impact 23°C 3.0mm Partial break | ISO 179 | kJ/m² | |
Charpy Notch Impact -30°C 3.0mm Complete Break | ISO 179 | kJ/m² | |
Charpy Un-notch Impact 23°C | ISO 179 | kJ/m² | |
Charpy Un-notch Impact -30°C | ISO 179 | kJ/m² | |
Charpy Un-notch Impact -60°C | ISO 179 | kJ/m² | |
Puncture Resistance Maximum Force 23°C | ISO 6603 | N | |
Puncture Resistance Maximum Force -30°C | ISO 6603 | N | |
Puncture Resistance 23°C | ISO 6603 | J | |
Puncture Resistance -30°C | ISO 6603 | J |
Optical performance | Standard | Value | Unit |
---|---|---|---|
Transmittance | ISO 13468 | % | |
Transmittance | ISO 13468 | % | |
Transmittance | ISO 13468 | % | |
Transmittance | ISO 13468 | % | |
Haze 3000.00μm | ISO 14782 | % | |
Refractive Index | ISO 489 |
Thermal | Standard | Value | Unit |
---|---|---|---|
HDT 1.8MPa | ISO 75 | °C | |
HDT 0.45MPa | ISO 75 | °C | |
Vicat Softening Temperature 50°C/hr 50N | ISO 306 | °C | |
Vicat Softening Temperature 120°C/hr 50N | ISO 306 | °C | |
Glass Transition Temperature 10°C/min | ISO 11357 | °C | |
CLE Flow 23~55°C | ISO 11359 | cm/cm/°C | |
CLE xFlow 23~55°C | ISO 11359 | cm/cm/°C | |
Heat Conductivity Coefficient 23°C Crossflow 50RH | ISO 8302 | W/(m·K) | |
Flash Point | ASTM D1929 | °C | |
Ignition Point | ASTM D1929 | °C |
Electrical properties | Standard | Value | Unit |
---|---|---|---|
Volume Resistivity | IEC 60093 | Ω.m | |
Surface Resistivity | IEC 60093 | Ω | |
Dielectric Strength 1.0mm | IEC 60243 | KV/mm | |
Dielectric Constant 100Hz | IEC 60250 | ||
Dielectric Constant 1MHz | IEC 60250 | ||
Dissipation Factor 100Hz | IEC 60250 | ||
Dissipation Factor 1MHz | IEC 60250 | ||
CTI Solution A | IEC 60112 | V | |
CTI M Solution B | IEC 60112 | V | |
Electrolytic Corrosion | IEC 60426 | Rating |
Flammability | Standard | Value | Unit |
---|---|---|---|
GWIT 0.75mm | IEC 60695 | °C | |
GWIT 1.0mm | IEC 60695 | °C | |
GWIT 1.5mm | IEC 60695 | °C | |
GWIT 3.0mm | IEC 60695 | °C | |
GWFI 0.75mm | IEC 60695 | °C | |
GWFI 1.5mm | IEC 60695 | °C | |
GWFI 3.0mm | IEC 60695 | °C | |
Flame Rating All Color 0.75mm | UL94 | ||
Flame Rating All Color 1.5~2.4mm | UL94 | ||
Flame Rating All Color 2.5mm | UL94 | ||
Flame Rating All Color 3.0mm | UL94 | ||
Flame Rating All Color 6.0mm | UL94 | ||
Limiting Oxygen Index Method A | ISO 4589 | % | |
Burning Rate >=1.0 mm | ISO 3795 | mm/min | |
Needle Flame Test 1.50mm Method K | IEC 60695 | s | |
Needle Flame Test 2.00mm Method K | IEC 60695 | s | |
Needle Flame Test 3.00mm Method K | IEC 60695 | s | |
Needle Flame Test 1.50mm Method F | IEC 60695 | s | |
Needle Flame Test 2.00mm Method F | IEC 60695 | s | |
Needle Flame Test 3.00mm Method F | IEC 60695 | s |
UL | Standard | Value | Unit |
---|---|---|---|
UL FlameRating ALL 0.75mm | UL94 | ||
HWI ALL 0.75mm | UL 746A | PLC | |
HAI ALL 0.75mm | UL 746A | PLC | |
RTI Elec ALL 0.75mm | UL 746B | °C | |
RTI Imp ALL 0.75mm | UL 746B | °C | |
RTI Str ALL 0.75mm | UL 746B | °C | |
UL FlameRating ALL 1.5~2.4mm | UL94 | ||
HWI ALL 1.5~2.4mm | UL 746A | PLC | |
HAI ALL 1.5~2.4mm | UL 746A | PLC | |
RTI Elec ALL 1.5~2.4mm | UL 746B | °C | |
RTI Imp ALL 1.5~2.4mm | UL 746B | °C | |
RTI Str ALL 1.5~2.4mm | UL 746B | °C | |
UL FlameRating ALL 2.5mm | UL94 | ||
HWI ALL 2.5mm | UL 746A | PLC | |
HAI ALL 2.5mm | UL 746A | PLC | |
RTI Elec ALL 2.5mm | UL 746B | °C | |
RTI Imp ALL 2.5mm | UL 746B | °C | |
RTI Str ALL 2.5mm | UL 746B | °C | |
UL FlameRating ALL 3.0mm | UL94 | ||
HWI ALL 3.0mm | UL 746A | PLC | |
HAI ALL 3.0mm | UL 746A | PLC | |
RTI Elec ALL 3.0mm | UL 746B | °C | |
RTI Imp ALL 3.0mm | UL 746B | °C | |
RTI Str ALL 3.0mm | UL 746B | °C | |
UL FlameRating ALL 6.0mm | UL94 | ||
HWI ALL 6.0mm | UL 746A | PLC | |
HAI ALL 6.0mm | UL 746A | PLC | |
RTI Elec ALL 6.0mm | UL 746B | °C | |
RTI Imp ALL 6.0mm | UL 746B | °C | |
RTI Str ALL 6.0mm | UL 746B | °C | |
Comparative Tracking Index | IEC 60112 | PLC | |
Inclined Plane Tracking | UL 746 | kV | |
Dielectric Strength | ASTM D149 | KV/mm | |
HVTR | UL 746A | PLC | |
Arc Resistance | ASTM D495 | PLC | |
Dimensional Stability | UL746 | % | |
Outdoor Suitability | UL-746C |
Injection molding | Value | Unit |
---|---|---|
Dry Temperature | °C | |
Dry Time | hr | |
Water Content Control | % | |
Zone1 Temperature | °C | |
Zone2 Temperature | °C | |
Zone3 Temperature | °C | |
Nozzle Temperature | °C | |
Melt Temperature | °C | |
Melt Temperature Optimum | °C | |
Mould Temperature | °C | |
Screw Speed | m/s | |
Shot to Cylinder Size | % | |
Back Pressure | bar | |
Holding Pressure | % | |
Vent Depth | mm |
Disclaimer: [17Suzao] the data displayed on the data search platform of industrial materials is for the convenience of users, this data search platform shall not be responsible for the uncertainties and consequences caused by relevant information, such as brand, data, reference value and all other data and Suggestions.Therefore, if there is any doubt about the data, the users should confirm the reliability of the data with the manufacturer or purchaser before using the product.
请把您发现的问题反馈给我们,我们将尽快解决!
您的邮箱还未验证,点击发送验证邮件至您的邮箱
邮箱:{{userEmail}}
科思创 Makrolon® PC 2805物性表
您还未留邮箱,填写邮箱后使用该功能,